API Spec 5L |
GB/T9711-1997 |
SY/T5037-2000 |
管端外径
偏差 |
+2.38mm
-0.79mm |
+2.38mm
-0.79mm |
D<508 ±0.75%D or ±2.5min
D≥508 ±0.50%D or ±4.5min |
壁厚公差 |
D<508 +15.0%t-12.5%t
D≥508 +19.5%t-8.0%t |
D<508 +15.0%t-12.5%t
D≥508 +17.5%t-10.0%t |
D<508 ±12.5%t
D≥508 ±10.0%t |
焊缝余高 |
≤3.18mm |
≤3.18mm |
t≤12.5 t≤3.2mm
t>12.5 t≤4.8mm |
直 度 |
≤0.2%L |
≤0.2%L |
≤0.2%L |
管端状态 |
坡口角30°-- 35°
顿边1.59±0.79mm
切斜≤1.59mm |
坡口角30°-- 35°
顿边1.59±0.79mm
切斜≤1.59mm |
坡口角30°-- 35°
顿边1.59±0.79mm
切斜≤1.59mm |
随圆度 |
D>508 ±1.0%D |
D>508 ±1.0%D |
D>508 ±1.0%D |
无损探伤 |
100% X射线或100%超声波加管端Ｘ射线检验。 |
距管端203mm以内的焊缝采用射线检验；距管端203mm以外的焊缝采用超声波检验；对头焊缝、补焊及环向焊缝采用超声波检验 |
补焊焊缝、对头焊缝及环向焊缝采用Ｘ射线或超声波检验。对原始焊缝应进行100%Ｘ射线或超声波检验或进行抽查 |
水压实验 |
P=2St/D |
P=2St/D |
P=2St/D |
备 注 |
D:钢管公称外径,mm t:钢管公称壁厚,mm
S:水压试验应力,Mpa P:静水压试验压力,Mpa
L;单根钢管长度，mm
|